261 Low Working Temperature Silver Cadium Free Alloy Tensile 60000 32% Elongation 19% Iacs High Silver Content High Detergent Flux
(Pack of
6)
SKU:EG26170000 Item#: EG26170000
A low working temperature silver brazing alloy with superb wetting action on difficult-to-join metals such as tool steels, stainless steel, beryllium copper and nickel alloys.
• Fast Flowing – Works well on tight joints
• High Silver Content – Lower melting point and reduces need for high heat for joining
• High-detergent conductivity
• High strength
• Corrosion resistant
• Cadmium-free
• Joint Strength: Up to 60,000 PSI/414 Mpa
• Elongation: 32%
• Working Temperature: 1370°F/743°C
• Electrical Conductivity: 19% IACS
• Corrosion Resistance: Good
• Coating: Blue
PROCEDURES Clean the weld area. Remove all rust, paint, grease, oil and other foreign matter. Maintain joint clearance of 0.003” to 0.005”. Prefluxing is not required; however, additional flux will help in tight joints and may be needed. Heat the weld area to a dull red color using a slightly carburizing flame. Melt off a small amount of alloy and flux. Keep the torch in motion and flow the deposit through the joint. Allow to cool slowly. Remove flux residue with warm water.
Frequently Bought Together
241 Premium Aluminum Brazing Alloy 1/8x36
Couldn't load pickup availability
41 Silver Flux Coated Brazing Rod 3/32"
Couldn't load pickup availability
40 Silver Flux Coated Brazing Rod 1/16"
Couldn't load pickup availability
SAE/Metric 3/8 Socket Blow Molded Case (*Empty Case Only)
Couldn't load pickup availability
2.1 Round Head Ratchet 3/8 Drive 168 Tooth
Couldn't load pickup availability
8" Dual Jaw Adj and Pipe Wrench
Couldn't load pickup availability
USS Flat Washer Thru-Hardened Steel 5/16"
Couldn't load pickup availability
Stepdown Butt Connector 22 to 18/16 to 14 AWG
Couldn't load pickup availability
Butt Connector 22 to 18 AWG Red
Couldn't load pickup availability
265 Bare Silver Free Flowing Copper Alloy .050X20
Couldn't load pickup availability
264 Bare High Silver Cadium Free Alloy 1/16x18
Couldn't load pickup availability
41 Silver Flux Coated Brazing Rod 1/16"
Couldn't load pickup availability
338 Mild/Carbon Steel Stick Rod Electrode 1/8"
Couldn't load pickup availability
176 Extreme Abrasion With Impact 1/4X18IN
Couldn't load pickup availability
E7018 Mild/Carbon Steel Stick Electrode 1/8"
Couldn't load pickup availability
Product Description
A low working temperature silver brazing alloy with superb wetting action on difficult-to-join metals such as tool steels, stainless steel, beryllium copper and nickel alloys.• Fast Flowing – Works well on tight joints
• High Silver Content – Lower melting point and reduces need for high heat for joining
• High-detergent conductivity
• High strength
• Corrosion resistant
• Cadmium-free
• Joint Strength: Up to 60,000 PSI/414 Mpa
• Elongation: 32%
• Working Temperature: 1370°F/743°C
• Electrical Conductivity: 19% IACS
• Corrosion Resistance: Good
• Coating: Blue
PROCEDURES Clean the weld area. Remove all rust, paint, grease, oil and other foreign matter. Maintain joint clearance of 0.003” to 0.005”. Prefluxing is not required; however, additional flux will help in tight joints and may be needed. Heat the weld area to a dull red color using a slightly carburizing flame. Melt off a small amount of alloy and flux. Keep the torch in motion and flow the deposit through the joint. Allow to cool slowly. Remove flux residue with warm water.
Technical Specifications
| Item#: | EG26170000 |
|---|---|
| Welding Process | Brazing |
| Type | Flux-Coated Brazing Rod |
| Diameter | 1/16 " |
| Length | 18 " |
| Tensile Strength | 70,000 PSI |
| Melting Temperature | 1,295 °F |
| Color | Blue |
| Base Metal | All Metals Except White Metals |
| Recommended Flux | 361 |
| UNSPSC #: | 23271804 |
| TAA Compliant: | Yes |
| Weight: | 0.395 lb |