510 Aluminum TIG Wire 1/8"
(Pack of
2.0)
Highly versatile alloys for all weldable types of aluminum including sheet, forgings, extrusions and castings.
Superior Advantages
• Stable, quiet arc with no undercutting
• Good corrosion resistance
Tensile Strength: 35,000 PSIPolarity: AC/High FrequencyGas: Argon/Helium
Usage ProcedureBevel heavy sections to allow 100% weld metal penetration. Sprinkle F56 flux into the joint area. Broadly heat area to be brazed with a large, soft and slightly carburizing flame to about 1,100°F (593°C). Heat the base metal until flux flows freely. The alloy will then begin to wet the base metal. Deposit the 510T to fill the joint. Flux residue may be removed with warm water and a brush.
Couldn't load pickup availability
California Proposition 65: WARNING: Cancer and Reproductive Harm -
www.P65Warnings.ca.gov
Catalog Page#: 13-16
Frequently Bought Together
510 Aluminum MIG Welding Wire 0.035"
Couldn't load pickup availability
ER5356 Aluminum MIG Welding Wire 0.035"
Couldn't load pickup availability
241T Aluminum Solid Tig Wire 3/32X36
Couldn't load pickup availability
SAE J995C Locknut with Nylon Insert Grade 8 3/8-16
Couldn't load pickup availability
Flat Washer Grade 12 Thru-Hardened Steel M8
Couldn't load pickup availability
SAE Flat Washer Thru-Hardened Steel 5/8"
Couldn't load pickup availability
Pipe Wrap Around
Couldn't load pickup availability
Anti Splatter Heat Resitant Welding Mat
Couldn't load pickup availability
Light Weight Composite Wear Plates 4X4X13/64
Couldn't load pickup availability
321 Mild and Carbon Steel MIG Welding Wire 0.024"
Couldn't load pickup availability
360 Mild and Carbon Steel Stick Rod Electrode 1/8"
Couldn't load pickup availability
1100 Gouging and Cutting Stick Rod Electrode 1/4"
Couldn't load pickup availability
Product Description
Highly versatile alloys for all weldable types of aluminum including sheet, forgings, extrusions and castings.Superior Advantages
• Stable, quiet arc with no undercutting
• Good corrosion resistance
Tensile Strength: 35,000 PSIPolarity: AC/High FrequencyGas: Argon/Helium
Usage ProcedureBevel heavy sections to allow 100% weld metal penetration. Sprinkle F56 flux into the joint area. Broadly heat area to be brazed with a large, soft and slightly carburizing flame to about 1,100°F (593°C). Heat the base metal until flux flows freely. The alloy will then begin to wet the base metal. Deposit the 510T to fill the joint. Flux residue may be removed with warm water and a brush.
Technical Specifications
| Item#: | CW1014 |
|---|---|
| Welding Process | TIG |
| Type | Solid |
| Diameter | 1/8 " |
| Length | 36 " |
| Tensile Strength | 35,000 PSI |
| Base Metal | Aluminum |
| Shielding Gas | 100% Ar |
| Polarity | AC High Freq |
| UNSPSC #: | 23271810 |
| TAA Compliant: | Yes |
| Weight: | 2.0 lb |