Xl Gold Dissimilar Metals Flux Core Mig Wire Tensile 122000 Gas 98% Ar 2%Co2 75Ar 2%Co2 Polarity Dcep 22-28Rc
(Pack of
33)
Designed for welding all steels manganese, stainless, AR plate, high-carbon and dissimilar combinations
Superior welding speed three times faster than stick welding and over 1-3/4 times faster than solid wires
High recovery rate over 90% deposition efficiency
Low heat input means less distortion and better tolerance control
All-position
Self-lifting slag
Tensile strengt: as deposited 122,000 psi/841 MPa
Yield strength: as deposited 92,000 psi/634 MPa
Elongation: 25%
Hardness: As deposited 22-28Rc/work-hardened 31-37Rc
Service temperature: 500°F/260°C
Gas: 100% CO2 or 75% Ar/25% CO2 or 98% Ar/2% O2
Current: DCEP (DC+)
Frequently Bought Together
333 Dissimilar Steel Stick Rod Electrode 5/32"
Couldn't load pickup availability
333 Dissimilar Steel Stick Rod Electrode 1/16"
Couldn't load pickup availability
Dissimilar Steel Stick Rod Electrode Kit
Couldn't load pickup availability
Flat Washer Grade 12 Thru-Hardened Steel M8
Couldn't load pickup availability
SAE J995C Locknut with Nylon Insert Grade 8 3/8-16
Couldn't load pickup availability
Lawson Open & Shut Nut & Bolt Loosener, Rust Penetrant, SKU DA6152, 20 oz Aerosol Can
Couldn't load pickup availability
E7018 Mild/Carbon Steel Stick Electrode 1/8"
Couldn't load pickup availability
Rosin Core Solder 0.032"
Couldn't load pickup availability
201 Rectangular Wear Disc Plate 3 x 6 x 5/32"
Couldn't load pickup availability
556 Aluminum TIG Wire 1/16"
Couldn't load pickup availability
510 Aluminum TIG Wire 1/8"
Couldn't load pickup availability
707 Dissimilar Steel Stick Rod Electrode 3/32"
Couldn't load pickup availability
Product Description
Designed for welding all steels manganese, stainless, AR plate, high-carbon and dissimilar combinations Superior welding speed three times faster than stick welding and over 1-3/4 times faster than solid wires
High recovery rate over 90% deposition efficiency
Low heat input means less distortion and better tolerance control
All-position
Self-lifting slag
Tensile strengt: as deposited 122,000 psi/841 MPa
Yield strength: as deposited 92,000 psi/634 MPa
Elongation: 25%
Hardness: As deposited 22-28Rc/work-hardened 31-37Rc
Service temperature: 500°F/260°C
Gas: 100% CO2 or 75% Ar/25% CO2 or 98% Ar/2% O2
Current: DCEP (DC+)
Technical Specifications
| Item#: | EG60380062 |
|---|---|
| Welding Process | MIG |
| Type | Flux-Cored Wire |
| Diameter | .062 " |
| Tensile Strength | 122,000 PSI |
| Yield Strength | 92,000 PSI |
| Elongation | 25 % |
| Hardness | 31-37 HRC |
| Shielding Gas | 75% Ar/25% CO2 or 100% CO2 |
| Polarity | DCEP |
| UNSPSC #: | 23271810 |
| TAA Compliant: | Yes |
| Weight: | 37.67 lb |