23 Copper and Steel Flux Coated Brazing Rod 3/32"
(Pack of
5)
Get strong, machinable joints on cast iron and sheet metal with the 23 Copper and Steel Flux Coated Brazing Rod. This versatile, thin-flowing alloy creates solid, dense deposits perfect for everything from auto body repairs to engine blocks, ensuring a tough repair without diluting the base metal. With a tensile strength of up to 68,000 PSI, this blue flux-coated rod provides superior welding performance for piping, gears, and more. Make your next project a success with reliable, high-strength bonds.
• Solid, dense deposits that can be machined
• Free-flowing for thin lapping and butted metal joining
• No base metal dilution making tough cast iron repairs possible
Flux Coating Color: BlueTensile Strength: Up to 68,000 PSIBonding Temperature: 1,400°F to 1,600°F (760°C to 871°C)Recommended Flux: F21 (if needed)
Typical Applications
• Sheet metal and auto body repairs
• Engine heads and blocks
• Piping, plumbing and pumps
• Gears, sprockets and pulleys
Usage ProcedureClean joint areas thoroughly. Heat metal with neutral flame until flux liquifies. Base metals should be dull red as Cronabraze™ 30F commences to penetrate the joint. Use rapid weaving motion with torch to deposit alloy drop-by-drop. Do not concentrate heat enough to melt base metal. Remove flux residue with water.
Frequently Bought Together
51 High Silver Flux Coated Brazing Rod 1/16"
Couldn't load pickup availability
23 Copper and Steel Flux Coated Brazing Rod 1/8"
Couldn't load pickup availability
30 Copper and Steel Flux Coated Brazing Rod 1/16"
Couldn't load pickup availability
SAE J995C Locknut with Nylon Insert Grade 8 3/8-16
Couldn't load pickup availability
IFI 100/107 Top Locknut Grade C 5/8-11
Couldn't load pickup availability
Hex Nut Grade 8 Alloy Steel 3/8-16
Couldn't load pickup availability
22 Cast Iron Bare Brazing Rod 3/16"
Couldn't load pickup availability
30 Copper and Steel Flux Coated Brazing Rod 3/32"
Couldn't load pickup availability
30 Copper and Steel Flux Coated Brazing Rod 1/8"
Couldn't load pickup availability
331 Mild and Carbon Steel MIG Welding Wire 0.035"
Couldn't load pickup availability
ER70S-6 Mild/Carbon Steel MIG Welding Wire 0.03"
Couldn't load pickup availability
ER70S-6 Mild/Carbon Steel MIG Welding Wire 0.035"
Couldn't load pickup availability
Product Description
Get strong, machinable joints on cast iron and sheet metal with the 23 Copper and Steel Flux Coated Brazing Rod. This versatile, thin-flowing alloy creates solid, dense deposits perfect for everything from auto body repairs to engine blocks, ensuring a tough repair without diluting the base metal. With a tensile strength of up to 68,000 PSI, this blue flux-coated rod provides superior welding performance for piping, gears, and more. Make your next project a success with reliable, high-strength bonds.• Solid, dense deposits that can be machined
• Free-flowing for thin lapping and butted metal joining
• No base metal dilution making tough cast iron repairs possible
Flux Coating Color: BlueTensile Strength: Up to 68,000 PSIBonding Temperature: 1,400°F to 1,600°F (760°C to 871°C)Recommended Flux: F21 (if needed)
Typical Applications
• Sheet metal and auto body repairs
• Engine heads and blocks
• Piping, plumbing and pumps
• Gears, sprockets and pulleys
Usage ProcedureClean joint areas thoroughly. Heat metal with neutral flame until flux liquifies. Base metals should be dull red as Cronabraze™ 30F commences to penetrate the joint. Use rapid weaving motion with torch to deposit alloy drop-by-drop. Do not concentrate heat enough to melt base metal. Remove flux residue with water.
Technical Specifications
| Item#: | CW1003 |
|---|---|
| Welding Process | Brazing |
| Type | Flux Coating |
| Diameter | 3/32 " |
| Length | 18 " |
| Tensile Strength | 68,000 PSI |
| Melting Temperature | 1560-2000 °F |
| Color | Blue |
| Base Metal | Copper/Steel |
| Recommended Flux | F21 |
| Description | All Purpose |
| UNSPSC #: | 23271804 |
| TAA Compliant: | No |
| Weight: | 5.5 lb |
Product Restrictions