52 Aluminum/Zinc Bare Brazing Rod, Gray, 18" Length, 1/8"
(Pack of
2)
SKU:CW1735 Item#: CW1735
A selection of alloys for joining all types of aluminum.
Superior Advantages
• Products for joining and buildup
• Easy to apply
High-strength, self-fluxing
Tensile Strength: 40,000 PSI
Bond Strength: 28,000 PSI
Application Temperature: 720°F (382°C)
Typical Applications
• Aluminum frames
• Tubing and piping
• Ornamental aluminum
• Cast aluminum
Usage ProcedureHeat base metal with 1-X acetylene feather flame. Melt off small amount of Cronabraze Eagle™ 52 and scrub (tin) area of repair using a clean stainless steel wire brush. Use circular motion of torch when applying buildup or repair alloy. Copper or carbon block is suggested as a chill bar when soldering thin sections. No flux is required.
Technical TipMaximum bonding requires getting to the base metal under the oxide layer present on all aluminum. To bond to virgin metal, scrub the bonding area with molten ‘52’ alloy or scratch the area with the ‘52’ alloy with the base metal at application temperature. Heavy oxide layers can be easily removed with ‘Flex’ grinding wheels.After tinning, bring filler to surface at 90° angle and manipulate torch in a circular motion at 45°. Avoid overheating base metal. Use clean torch tip to p
Frequently Bought Together
241 Premium Aluminum Brazing Alloy 1/8x36
Couldn't load pickup availability
241 Premium Aluminum Brazing Alloy 1/16x36
Couldn't load pickup availability
53 Pot Metal Bare Brazing Rod 1/16"
Couldn't load pickup availability
54 Aluminum Flux Cored Brazing Rod 1/8"
Couldn't load pickup availability
47 Sil-Phos Bare Brazing Rod 1/8"
Couldn't load pickup availability
51 High Silver Flux Coated Brazing Rod 1/16"
Couldn't load pickup availability
3/16" - 1/2" Cryonitride Spiral Fluted Step Drill - 5/16" Shank
Couldn't load pickup availability
CryoBoost 1/2" Dia. 1/4" Hex Shank Drill Bit
Couldn't load pickup availability
Hex Cap Screw Grade 9 Alloy Steel 9/16-12 x 2-1/2"
Couldn't load pickup availability
Self-Drilling Screw Hex Head #10-16 x 3/4"
Couldn't load pickup availability
Flat Washer Grade 12 Thru-Hardened Steel M10
Couldn't load pickup availability
SAE J995C Locknut with Nylon Insert Grade 8 5/8-11
Couldn't load pickup availability
Wear Plates Used By Maintenance Welder 1/4X4X5
Couldn't load pickup availability
163 Arc-Cut Synthetic Carbon Arc Electrode
Couldn't load pickup availability
ER70S-6 Mild/Carbon Steel MIG Welding Wire 0.03"
Couldn't load pickup availability
Product Description
A selection of alloys for joining all types of aluminum.Superior Advantages
• Products for joining and buildup
• Easy to apply
High-strength, self-fluxing
Tensile Strength: 40,000 PSI
Bond Strength: 28,000 PSI
Application Temperature: 720°F (382°C)
Typical Applications
• Aluminum frames
• Tubing and piping
• Ornamental aluminum
• Cast aluminum
Usage ProcedureHeat base metal with 1-X acetylene feather flame. Melt off small amount of Cronabraze Eagle™ 52 and scrub (tin) area of repair using a clean stainless steel wire brush. Use circular motion of torch when applying buildup or repair alloy. Copper or carbon block is suggested as a chill bar when soldering thin sections. No flux is required.
Technical TipMaximum bonding requires getting to the base metal under the oxide layer present on all aluminum. To bond to virgin metal, scrub the bonding area with molten ‘52’ alloy or scratch the area with the ‘52’ alloy with the base metal at application temperature. Heavy oxide layers can be easily removed with ‘Flex’ grinding wheels.After tinning, bring filler to surface at 90° angle and manipulate torch in a circular motion at 45°. Avoid overheating base metal. Use clean torch tip to p
Technical Specifications
| Item#: | CW1735 |
|---|---|
| Welding Process | Brazing |
| Type | Bare Brazing Rod |
| Diameter | 1/8 " |
| Length | 18 " |
| Tensile Strength | 28,000 PSI |
| Melting Temperature | 720 °F |
| Base Metal | Aluminum/Zinc |
| UNSPSC #: | 23271804 |
| TAA Compliant: | Yes |
| Weight: | 2.5 lb |
Product Restrictions