54 Flux Cored Brazing Rod, 32" Length, 1/8" Diameter, Aluminum
(Pack of
2)
SKU:CW1857 Item#: CW1857
A selection of alloys for joining all types of aluminum.
Superior Advantages
• Products for joining and buildup
• Easy to apply
Flux-cored for all types of aluminum
Tensile Strength: 34,500 PSIApplication Temperature: 1,110°F (599°C)Recommended Flux: F56 (if needed)
Typical Applications
• Aluminum frames
• Tubing and piping
• Ornamental aluminum
• Cast aluminum
Usage ProcedureBevel heavy sections to allow 100% weld metal penetration. Broadly heat area to be brazed with a large, soft and slightly carburizing flame to about 1,050°F (566°C). Warm the end of the rod and rub on base metal until flux flows freely. 54C will then begin to wet the base metal. Deposit the 54C to fill the joint. Flux residue may be removed with warm water and brush. If additional flux is needed, use F56 flux.
Couldn't load pickup availability
Catalog page#: 13-29
Frequently Bought Together
52 Aluminum/Zinc Bare Brazing Rod 1/8"
Couldn't load pickup availability
53 Pot Metal Bare Brazing Rod 1/16"
Couldn't load pickup availability
261 Blue Flux Coated General Purpose Silver Brazing Alloy 1/16X18
Couldn't load pickup availability
265 Bare Silver Free Flowing Copper Alloy .050X20
Couldn't load pickup availability
264 Bare High Silver Cadium Free Alloy 1/16x18
Couldn't load pickup availability
Flat Washer Grade 12 Thru-Hardened Steel M8
Couldn't load pickup availability
PTO Pin Lock 1/4 x 2-1/2"
Couldn't load pickup availability
Locknut with Nylon Insert Grade 8 5/16-18
Couldn't load pickup availability
ER70S-6 Mild/Carbon Steel MIG Welding Wire 0.03"
Couldn't load pickup availability
45 Silver Bare Brazing Rod 1/8"
Couldn't load pickup availability
Rosin Core Solder 0.032"
Couldn't load pickup availability
Product Description
A selection of alloys for joining all types of aluminum.Superior Advantages
• Products for joining and buildup
• Easy to apply
Flux-cored for all types of aluminum
Tensile Strength: 34,500 PSIApplication Temperature: 1,110°F (599°C)Recommended Flux: F56 (if needed)
Typical Applications
• Aluminum frames
• Tubing and piping
• Ornamental aluminum
• Cast aluminum
Usage ProcedureBevel heavy sections to allow 100% weld metal penetration. Broadly heat area to be brazed with a large, soft and slightly carburizing flame to about 1,050°F (566°C). Warm the end of the rod and rub on base metal until flux flows freely. 54C will then begin to wet the base metal. Deposit the 54C to fill the joint. Flux residue may be removed with warm water and brush. If additional flux is needed, use F56 flux.
Technical Specifications
| Item#: | CW1857 |
|---|---|
| Welding Process | Brazing |
| Type | Flux Cored |
| Diameter | 1/8 " |
| Length | 32 " |
| Tensile Strength | 34,500 PSI |
| Melting Temperature | 1560-2000 °F |
| Base Metal | Aluminum |
| Recommended Flux | F56 |
| UNSPSC #: | 23271804 |
| TAA Compliant: | Yes |
| Weight: | 2.5 lb |