53 Pot Metal Bare Brazing Rod 1/8"
(Pack of
2.0)
Easily joins white and pot metals.
Superior Advantages
• Lead- and cadmium-free
• Extremely low melting point
• Two times stronger than ordinary solder
Low temperature, dissimilar pot metal
Tensile Strength: 17,500 PSIApplication Temperature: 360°F (182°C)Recommended Flux: F53
Typical Applications
• Air conditioning and refrigeration units
• Brazing/soldering of copper to aluminum, brass to steel, stainless to zinc, etc.
Usage ProcedureBase metal must supply heat, as a direct flame is unworkable. A carburizing flame should be used. A flux is required for all applications where good bonding is desired.
Technical TipDo not direct torch at flux, as it will char. Allow CRONABRAZE 53 to solidify before quenching and removing flux residue. CRONASOLV™ F53 flux is recommended for all applications.
Couldn't load pickup availability
California Proposition 65: Not Applicable
www.P65Warnings.ca.gov
Catalog page#: 13-30
Frequently Bought Together
241 Premium Aluminum Brazing Alloy 1/16x36
Couldn't load pickup availability
54 Aluminum Flux Cored Brazing Rod 1/8"
Couldn't load pickup availability
52 Aluminum/Zinc Bare Brazing Rod 1/8"
Couldn't load pickup availability
30 Copper and Steel Flux Coated Brazing Rod 1/16"
Couldn't load pickup availability
44 Silver Bare Brazing Rod 1/16"
Couldn't load pickup availability
41 Silver Flux Coated Brazing Rod 1/16"
Couldn't load pickup availability
Hex Nut Grade 8 Alloy Steel 3/8-16
Couldn't load pickup availability
PTO Pin Lock 1/4 x 2-1/2"
Couldn't load pickup availability
IFI 100/107 Top Locknut Grade C 5/8-11
Couldn't load pickup availability
11-45 MIG Welding Contact Tip 0.045"
Couldn't load pickup availability
556 Aluminum TIG Wire 1/16"
Couldn't load pickup availability
707 Dissimilar Steel Stick Rod Electrode 3/32"
Couldn't load pickup availability
Product Description
Easily joins white and pot metals.Superior Advantages
• Lead- and cadmium-free
• Extremely low melting point
• Two times stronger than ordinary solder
Low temperature, dissimilar pot metal
Tensile Strength: 17,500 PSIApplication Temperature: 360°F (182°C)Recommended Flux: F53
Typical Applications
• Air conditioning and refrigeration units
• Brazing/soldering of copper to aluminum, brass to steel, stainless to zinc, etc.
Usage ProcedureBase metal must supply heat, as a direct flame is unworkable. A carburizing flame should be used. A flux is required for all applications where good bonding is desired.
Technical TipDo not direct torch at flux, as it will char. Allow CRONABRAZE 53 to solidify before quenching and removing flux residue. CRONASOLV™ F53 flux is recommended for all applications.
Technical Specifications
| Item#: | CW1017 |
|---|---|
| Welding Process | Brazing |
| Type | Bare Brazing Rod |
| Diameter | 1/8 " |
| Length | 18 " |
| Tensile Strength | 17,500 PSI |
| Melting Temperature | 360 °F |
| Base Metal | Pot Metal |
| Recommended Flux | F53 |
| UNSPSC #: | 23271804 |
| TAA Compliant: | Yes |
| Weight: | 2.25 lb |
Product Restrictions
California Proposition 65: Not Applicable
www.P65Warnings.ca.gov